Luminophor Pigment with High Luminous

1.self luminous ,photoluminescent pigment 2. rare earth metal high brightness 3. long afterglow time 4. lower heavy metal

What is photoluminescence?Lightlead photoluminescent materials (commonly called “glow-in-the-dark”) has the ability to absorb light (sunlight, fluorescent, incandescent,etc) and then to emit light. 

When ambient darkness occurs, it becomes highly visible, lasting at least 8 hours. Our best products 

could last more than 20 hours. Upon removal of the light source, the stored light is gradually released, the strongest glow is produced during 

the first 30 minutes of darkness, the most critical period following a power failure or other emergency. Then it fades

 over a period of time, when there is light again, it stores energy again. So the photoluminescence process is 

circulatory. The bases of most photoluminescent products are photoluminescent pigments that can be incorporated into coat, 

paint, ink, fabric, ceramic glaze or porcelain enamel, glass, flexible and rigid molded plastics. Typical products 

include self adhesive flexible vinyl tapes, rigid PVC marker strips, and silkscreened signage. 

Photoluminescent fabric, enamel-coated sheet metal and ceramic tiles are also available.

What is Strontium Aluminate pigment?Recent research efforts have produced several new inorganic compounds whose photometric characteristics 

greatly exceed those of zinc sulphide compounds. These materials include oxides of strontium aluminate 

(identified as SrAl) and other proprietary inorganic compounds. These compounds offer much brighter and longer-lasting photoluminescence, and they can formulate (unlike zinc sulphide compounds) to produce a range of colors.

How to make glow in plastic

Application in plastic:

1. This new type of luminous powder of is compatible with acrylic, polyester, epoxy, PVC, polypropylene and polyethylene (HDPE, LDPE etc.) polymers.

2. Material can be cast, dipped, coated, extruded or molded. 

3. Preferably use master batches or compounds for incorporating luminous powder into plastics.

4. As luminous material is a very hard substance and the particles have a needle like shape, it is difficult to incorporate into plastic resins directly. 

5. It is recommended to use an extruding temperature as low as possible. 

6. Master batches containing luminous material must be fully dried up before usage. 

7. Plan on using less than classical phosphorescent pigment loading. 

Luminophor Pigment with High Luminous